Epoxyden HB AF Anti-flame 755 + 931. Denber paints and coatings

Epoxyden HB AF Anti-flame 755 + 931

Fire retardant protection thick coat for casting 82% solids

Special thick coat to prevent fire expansion in case of fire, transparent and tinted decorative thick layer to use for powerful coating on printed circuits in electronics, for protecting concrete and parquet floors, thick coat for protecting metals, for coating composed materials against fire.

* Tested by the standards institution of Israel-standard 755

Epoxyden HB AF Anti-flame 755 + 931. www.denber-paints.co.il

Epoxyden HB AF Anti-flame 755 + 931

Fire retardant protection thick coat for casting 82% solids

Properties:

Fire protection coat.
High pressure and scratches resistance.
Good adhesion to metal, concrete, wood and any dry and not smooth infrastructure.
Contents 18% soft solvents.
82% solids.
Appropriate for using on printed circuits.
Appropriate for coating floors in industry.
Can be applied in one thick layer
In red brown/grey/black/ocher colors it is also rust resistance.
Tree elements: in Varnish transparent tints or clear for wooden floors and wooden objects and in many colors according catalog.
Can be implemented in thin layers.
Prevent fire expansion.
Resistant to salt and dry environment.
Washable and repulsive dust & dirt.

Applications:

For painting iron metals to defend from melting in fire.
Wooden objects, roofs, walls and floors to prevent fire.
Electric transformations to prevent fire and vibrations.
Protection from fire spreading on printed circuits in the electronic industry.
For immediate treatment in places being used for works with life fire or welding executed.

Epoxyden HB AF Anti-flame 755 + 931

Fire retardant protection thick coat for casting 82% solids

Technical Data:

Theoretical spreading rate: 1 liter per 15 m 2·
Theoretical field: 6-7 m 2/liter for 150 mic.
Recommended layer thickness: Minimum 150 micron, maximum 1 cm.
Recommended number of layers: as much needed to coat or fill.
Density: 0.9-1.35 gm/cm 3··
Hardness: >3 Dg (Erichsen).
Elasticity: 4 mm (Sheen).
Viscosity: 2-4 Pa.sec (Haake).
Mixing rate a:b by volume: 1:1.33

Contains:

Special Epoxy resins rich with Flame retardants.
Flexibility materials.
High temperature resistant fillers.
Additives.
Solvents.
Hardeners.

Colors:

Transparent, black, red oxide, brown, dark green, dark yellow, gray and more …

Gloss:

Silk.

Epoxyden HB AF Anti-flame 755 + 931

Fire retardant protection thick coat for casting 82% solids

Touch-drying time:

60 minutes to a layer of 150 micron.

Repainting Gap Time:

12 hours, final- 36 (to a layer of 150 micron. for thick layers up to 3 days, and up to 7 days for layers of 4 cm and more thickness).

Recommended Application Methods:

Cast, brush.

Dilution:

No dilution.

Surface Preparation:

Metal:

Mechanical or chemical cleaning until a white metal appears.
Mechanical: steel brushes st-3 or sand blast SA-2.5
Chemical: rust -“rust remover 3000”, grease -“Degreazer M”.
Primer coat with Epoxyden primer antiflame.

Concrete:

Sand blast cleaning and vacuum.
Or acid burn and water high pressure cleaning.
Or polishing with diamond stones and vacuum.
Primer with Epoxyden floor primer antiflame.

Epoxyden HB AF Anti-flame 755 + 931

Fire retardant protection thick coat for casting 82% solids

Wood:

Sand well and clean.
Primer – Isolation primer antiflame.

Printed circuits:

Cleaning the surface with air pressure and pure isopropyl alcohol.

Kit Description:

0.75 liter, part A + 1 liter part B
1.9 liter, part A + 2.5 liter part B
3.8 liter, part A + 5 liter part B
15 liter, part A + 18 liter part B

Storage:

Appropriate shaded room temp. with proper ventilation.
Keep lids tightly closed.

Shelf Life:

12 months in original sealed package.

Tools cleaning:

Clean with thinner D-4/100 immediately after complete painting.

Quality control:

In factory laboratories according to specifications.
COA and COC certificate.
ISO 9001-2015

Epoxyden HB AF Anti-flame 755 + 931