Denbergloss antiflame flame retardant lacquer

Denbergloss antiflame flame retardant lacquer

Denbergloss Antifleem Standards Institute

Fire retardant varnish Danberglus Antipalim 2:1:1 transparent anti-fire varnish – base/top two-component transparent polyurethane that can be polished in the first layer to fill the purim with natural wood and light polishing before coating with top varnish “Danberglus Antipalim”. Used as a transparent and top element in a lacquer painting system for fire-protected wood/furniture. Prevents the spread of fire in the event of a fire. For sealing and smoothing as a preparation before coating with varnish and as a finishing varnish layer.

DENBERGLOSS ANTIFLAME flame retardant LACQUER PRIMER AND TOP LAYER FOR WOODEN OBJECTS

Characteristics:

Three components to mix before use in a 2:1:1 ratio
quick drying.
Easy to rub on the first day after painting.
Seals and effectively fills the pores of the wood.
Coated with a layer of high-quality wear-resistant and UV-resistant varnish
For application in thin layers.
Prevents the spread of fire.
Flexible and hard.
Clear.

uses:

Flame retardant transparent base and top for painting quality furniture, parquets, wooden structures, floors and wooden ceilings.
Transparent base and top for domestic, public wood parquet floors and sports halls prevents the spread of fire.
Also a fire retardant transparent base and top for painting wooden sculptures, wooden wind boxes, pergolas and garden furniture, etc.
Also a transparent flame retardant base and top seal for antique and luxury furniture.

Transparent varnish against fire, standard Mati 755 – transparent polyurethane base/top for flame retardant wood.

Technical data:

Storage durability – 24 hours at 57 ⁰ without separation and spoilage,
Theoretical coverage – 1 liter per 6-10 square meters.
Practical coverage for a layer of 150 microns – 1 liter per 6-7 square meters.
Recommended layer thickness – 75 dry microns.
Recommended number of layers – 2
Flexibility – 1 mm (sheen)
Density – 9-1.1gm/cm ³
Average viscosity A+B – 2-4 sec
Stiffness – 3 Dg (Ericsson)
Base to hard ratio – 2:1
Durability time of diluted paint in the package – 6 hours (viscosity increase no more than 6 seconds from original viscosity)
Tahina minutes – Mat 5 > Hagman
Barak at 60 ⁰ – matte >5%
Pot life = working time from the moment of mixing B+A – 4> hours.
Humidity chamber – 30 days in 100% humidity at a temperature of ^O C49 without loss of adhesion or damage to the film one hour after removal from the liquid
Thermal market – no loss of adhesion.
% solids by volume – 66%

variety:

Clear. and

Lightning:

Matt. and
silk. and

Touch drying :

20 minutes

Drying between layers:

20 minutes, final drying – 8 hours.

and drying for polishing:

6 hours.

Application methods:

Brushing, rolling, spraying.

Dilution:

To spray – 10-20% thinner 11 – D pressure 3-4 at’.
Brushing/rolling – can be applied without thinning or up to 20% in thinner 11 – D
In the summer, to slow down drying if OVER SPRAY is formed, it is recommended to add a retarder.
Airless – 5-10% thinner D-11 pressure 4-5 atm

packing:

1+0.5+0.5 = 2 liters
2+1+1= 4 liters
5+2.5+2.5 = 10 liters

This technical specification is for non-binding general information only. and