Epoxyden Ship EA-19 Aluminium 2:1 Denber paints & coatings

Epoxyden Ship EA-19 Aluminium 2:1

High build epoxy primer/mid. coat (power heavy duty)

Epoxyden Ship 19 aluminum barrier primer prevent humidity penetration

A two component anti-corrosive epoxy polyamine primer or mid. coat high build heavy duty. It is surface passive and for that re-coat able for a long period of time and can be painted in several layers to obtain the proper thickness to form durability against mechanical abrasion for long period of time. Durable in hard salty sea water and under water environment. Isolation coat that prevents the passing through of the moisture, for mid. isolation layer for pipes, ships, tankers, reservoirs before coating with top polyurethane paints or under water Antifouling paints. Suitable for painting over light rust or partial surface preparation. Can be applied in primer and mid coat 150 mic, each and together the 300 mic. coat are as strong as steel. Prepared for the continuation of the painting process as well as for Antifouling coatings.

Epoxyden Ship EA-19 Aluminium 2:1. www.denber-paints.co.il

Suitable for painting water pipes and tanks & tankers made of ferrous metal , producing anticorrosive sealing protective layer preventing the moisture to pass through .by painting several layers a thick coating is achieved with a mechanical durability for long time. Contains no lead, chromates or coal-tar. Contains aluminum flakes for barrier protection to steel and galvanize steel. Resistant to boiling water and to heat up to 200^OC.

Suitable to aggressive corrosive environment level C5-I and complies with the standard ISO 12944-6 for chemicals ISO 2812-1, humidity chamber ISO 6270, salt spray chamber ISO 7253, for DURABILITY LEVEL RANGE – HIGH

Epoxyden Ship EA-19 Aluminium 2:1

High build epoxy primer/mid. coat (power heavy duty)

Properties:

Strong & flexible multi thickness paint.

Suitable for painting over alight rusted steel with a partial prepared surface.
Anticorrosive, prevent developing of rust.
- Primer and middle layer for ships before painted with “Tutgum antifouling” in under water surfaces or “Denbergloss ship” for the upper surfaces.
- Not toxic and do not emits poison.
- Durable in boiling water and resistant to heat up to 200^O
- Durable in extreme humidity, sea water and underwater conditions.
- A primer with mechanical strength and has high adhesion to ferrous metals and galvanize metals.
- Durable in sea water.
- The primer has excellent adhesion ability to the surface and provides an excellent primer to pipes and reservoirs before top coat painting.
- The stricter of the aluminum flakes provides a barrier protection aloud no humidity to pass through.
- Anticorrosive, prevent oxidation and rust.
- Resistant to solutions of acids or of alkali also in extreme conditions of humidity and moisture.
- layer in painting systems of tankers for fuels and crude oil.
- Easy to apply, dries fast.
- Can be apply in many layers with an open time for recoat of 48 hours in brushing or spraying.
- Can be painted by brushing or spraying to create multi layers.
- Thixotropic, suitable to produce in each single spraying a thick layer.
- Low surface strength makes it easily recoat able – more layers can be applied or a top paint can be applied on the primer.

High build epoxy primer/mid. coat (power heavy duty)

Applications:

To paint intermediate/mid barrier layer, for vessels of all kind for sealing, and for corrosion and mechanical protection.
As primer before top polyurethane paints on exterior building walls from concrete or metal in humid environment or near the sea salted atmosphere.
For painting buildings / constructions made of steel in corrosive atmosphere of the chemical industry,
For painting interior and exterior surface of pipes and tankers for fresh and salted water.
For painting pipes and tankers of drinking and salt water contact in water desalination facilities.
For intermediate layer, mid coat, in tankers/containers of crude oil and its refined.
As mid. layer on zinc primer coat.

Epoxyden Ship EA-19 Aluminium 2:1

High build epoxy primer/mid. coat (power heavy duty)

Technical data:

Coverage – 1 liter to 15 sqm.
Coverage in 125 mic. recommended layer – 1 liter for 6 sqm.

Hiding power – a layer of 58 microns > 0.95
Flexibility – 1 mm (sheen)
Density – 1.50-1.65 gm\cm³ (ASTM D1475)
Viscosity part A + part B immediately after mixing – 6-8 Pa.sec , 45 seconds # 4
Hardness – >10 Dg (Erichsen)
Flash point – 38^OC
Solids by volume – mixed A+B= 75% by Vol., (ASTM-D-2369)
Erosion-120 microns film –5600 cycles (BYK Gardner) ASTM
Recommended layer thickness – 125 mic. dry film.
Recommended number of layers – 2-3 (surface passive – can apply many coats)
Pot life (working time from mixing a with b) – 0.5 – 1 hours. (After 4 hours blend B + A viscosity less than 70 seconds on cup 4 # after 8 hours will not show jell)
Mixing ratio A: B – 2 : 1 by volume.
Waiting time after mixture and before painting: no need
Heat resistance- for 1 hr. in 121^oc without changes of shade or quality of the film.
Hot oil durability – 121^oc for 24 hours without any changes in the quality of the film and the shade.
Oil hydraulic resistance point- 65^oc for 24 hours without any changes in the quality of film and it shade.

High build epoxy primer/mid. coat (power heavy duty)

Solvents durability – 50 cycles rubbing with cloth soaked in MEK – no peeling of paint.
Distilled water resistance – 4 days in 49^oc – no defects of film and adhesion.
Adhesion test – stick 3M standard tape to surface under pressure of 2 kg and after 1 hr. pull it off – no paint split off the surface.
Salt spray (with scratch) resistance – 3000 hr. (development corrosion up tp 5 mm ASTM B117-97 table 1 step 5)
Salt spray ISO 7253 – 1440 hr.with 5 cm scratch and at list 2 cm from panel edge

(3 panels in test 7x15cm, M < M=C-W =1 C- scratch size with corrosion

2 2 W- scratch size 50mm

Thickness tested – 250 mic. dry film. Will show no pilling, bubbles, other defects. Corrosion level will be less than 1 mm.

Humidity cabinet 720 hr. in 30 cycles for high durability. ISO 6270 – Will show no pilling, bubbles, other defects.
Humidity cabinet 3000 hr. panel coated 150 mic. with scratch (ASTM 1654-0 table 1 step 10) – zero rust from scratch.
Pull off adhesion test ASTM D4541 average result of 4 tests in thickness 110-125 micron average 117 microns, after 7 days drying – 850 Psi
Chemical resistance – ISO 2812-1 , 168 hr. in solutions: 10% NaOH, 10% H2SO4, turpentine with 18% aromatics, for tests Lm-1 water , Lm-2 sodium chloride 5% Will show no pilling, bubbles, other defects.

Epoxyden Ship EA-19 Aluminium 2:1

High build epoxy primer/mid. coat (power heavy duty)

Contains:

Epoxy resin and. (Siba-Geigi)
Fillers, anticorrosive pigments.
Polyamide hardeners for sea waters.
Aluminum flakes pigment filler.
Solvents and additives

Colors:

Metallic red/brown.

Gloss:

Mate <7% (ASTM D 523) 60^O lens test

Touch dry time:

1-2 hours. (Due to the quick drying time especially in summer hot day out doors – avoid from over spray, avoid spraying “dust”)

Drying between layers:

16 hours. Final drying: 24 hours.

Application methods:

Brush, roller, spray.
Spray gun – it is recommended inter pressure < 4 atm.
Airless – pressure 5-7 atm. dilution 0-5% nozzle 0.021 “

Thinning:

Thinner D-4/100. (MIL-T-81771 Type II)
5-10% by volume -according to need. if orange peel appearance you can increase the dosage to 35%
Spraying with spry gun – 15-20%
Airless – 0-5% nozzle 0.021-0.023”

Epoxyden Ship EA-19 Aluminium 2:1

High build epoxy primer/mid. coat (power heavy duty)

Surface preparation:

A thorough cleaning needed from dirt, dust and loose paints.
On old paint – sand well and clean with air pressure, clean with dry clean cloth soaked with thinner.
Iron Metals – recommended but not must – sand blast cleaning till white metal appears SA-2.5 level. Metal brushes clean -For rusty surfaces ST-3, for light rusty surfaces – ST-2.5, for galvanize steel – sanding until totally matte surface appears.
Very big surfaces –remove the paint with paint removers and wash with water for neutralizing. Sand/spray soft sands or plastic powder for light roughness. Rinse with water and dry completely.
For aluminum –burn with ANTAROX 4 and PASSIVATOR 1722 yellow/green, or spray layer of Epoxyden Stronzium Chromate MIL–C-23377 for best primer and this product as mid. Thick layer.

Primer:

This product itself is a primer and mid. coat.
For aluminum – “Epoxydem wash primer” or “Epoxyden Stronzium chromate”.

Top color:

“Denbergloss ship” and “Denbergloss acrylic” .

Instructions for use:

Open carefully parts A and B and stir separately.
Pour from two parts in the right ratio the required amount and mix well with mechanical mixer (operated by air pressure is recommended for safety reasons) for a uniform mixture.
Wait for 10 minutes while adding the thinner as needed and mix again. Spray a thin layer of 125microns thickness dry film. If necessary if the layer does not completely uniform or part of surface not painted, wait about 4-12 hours for complete drying (if not completely dry it can shrink) and spray another layer.

v Wash the equipment well immediately after finishing painting.

Pot Life after mixing the mixture a + b of 5 liters:

15^oc – 40 minutes
20^oc – 30 minutes.
25^oc – 25 minutes
30^oc – 20 minutes
35^oc – 15 minutes.

Epoxyden Ship EA-19 Aluminium 2:1

High build epoxy primer/mid. coat (power heavy duty)

Ventilation:

Quantity air needed for 1 liter of blend paint :
Achieving 10% of the LEL = 65M³
To obtain the TLV = 990 M³

Packaging:

3.35+1.65 = 5 liters.

Storage:

In cool and shaded room in room temp. with proper ventilation.
Keep lids tightly closed.

Shelf life:

24 months in original package.

Tools cleaning:

D- 4/100 thinner immediately after painting.

Quality control:

In factory laboratories according to specifications.
COA and COC certificate.
ISO 9001-2015

Epoxyden Ship EA-19 Aluminium 2:1

Safety precautions:

Inedible, keep away from the reach of children.
Flammable – keep distant from heated areas, fires, flames, and sparks, Prohibit smoking in working area.
While applying, good air ventilation is important. In case there is not enough air, use ventilation according to the ventilation table.
Wear protective glasses, gloves and suits.
Avoid direct contact of the paint and/or thinner with the eyes and skin. In case of contact, immediately wash thoroughly with water.
In case of an injury immediately get doctors assistance.
Read the safety instructions on the labels.
See M.S.D.S

Epoxyden Ship EA-19 Aluminium 2:1