EPOXYDEN SHIP COOPER ANTIFOULING

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.

Epoxy 100% solids with a high concentration of pure copper 99% that produces at sea Cooper Oxide, has a high sliding coefficient for painting sea crafts with a high and low cruising speed. For painting in the lower part below the level of the sea water to prevent fouling (adherence and accumulation of sea crops, algae, oysters, etc.,) Contains a high concentration of pure copper powder that produces regularly over many years cooper oxide that prevents fouling. The Cooper Oxide toxins prevents tumor adherence to the bottom of the ship for  long-term durability, this erosion of the coat of 250 micron can provide a 10 year protection to the to the bottom of the vessel. Contains no tin.

EPOXYDEN SHIP COOPER ANTIFOULING. www.denber-paints.co.il

EPOXYDEN SHIP COOPER ANTIFOULING. www.denber-paints.co.il

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.

Properties :

  • Environmentally friendly and contains no solvents and no tin compounds.
  • Very rich in copper and biocides and provides protection against fouling and different crops on the bottom of the vessel at high and low speeds cruise that slowness of the vessel.
  • Very strong adherence to primer Epoxyden Solcoat layers.
  • Produces in contact with sea water Cooper oxide which is a toxin that prevents the development of tumors at the bottom of the underwater level sea crafts (causing a slowdown in the speed of the vessels and waste of energy consuming to overcome unnecessary friction caused from the sticking of fouling on the bottom of the vessel).
  • Quick drying and multi-thickness, same day application has multiple layers thickness is desirable for prolonged protection. Re coat time short due to rapid drying.
  • Excellent adherence ability between layers.
  • Has the characteristics of self-grinding tiny 5 micron per year each time revealing a fresh new layer without fouling cumulative.
  • Resistant to heat and cold and extreme sea conditions salty sea water and fresh water.
  • Optimized friction in seawater cruise at slow and fast cruise, durable friction too rough ice and / or harbor walls.
  • Strong and is suitable for immersion in sea water and fresh water for many years and have characteristics of shocks resist any vessel gets.
  • Implementation by spray / roller. Not for brushing.
  • Dries quickly. You can apply 4-5 layers of 60 microns each one at a resistance of 10 years or more.

Applications:

  • Painting all types of large and small vessels made ​​of steel/fiberglass/wood /aluminum in there under water level.
  • Painting yachts, tug boats route rand service boats,barges,fishing and racing boats, cargo ships, passenger ships and .

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.

Technical data:

  • Part A – can be mixed easily, and in 5 minutes you’ll receive a smooth and uniform solution.
  • Part B–transparent and clear.
  • Storage durability – 24 hours at 570 C with no sagging or corruption.
  • Theoretical coverage – 1 liter to 4 sqm. in 250 microns dry layer.
  • Thickness of layer- Must be apply in 4-5 coats of 60-65 micron..
  • Elasticity – 5 mm (sheen)
  • Density – 1.9-2.1 gm\cm3
  • Viscosity average A + B – 3-3.5 Pa. sec
  • Hardness – >10 Dg (Ericsson)
  • Erosion – 120 microns – 1550 cycles (BYK Gardner) ASTM
  • Ratio – 1 base to 0.4 hardener to 0.7 cooper powder.
  • Pot life = working time from mixing B + A – <20 minutes.
  • Distilled water resistance for 24 hr. – without losing adhesion or corrosion 1 hr. after taking out of water.
  • Carbon resistance – no loss of adhesion durability 1 after taking out of the solvent.
  • Resistance to oil 1250 24 hours in 121oC – no loss of adhesion 4 hours after taking out of the oil.

High build self-eroding 99% pure cooper and cooper oxide.

  • Hydraulic oil resistance  24 in 66oC – without losing adhesion 4 hours after taking out of the oil.
  • Aviation Fuel resistance – 7 days in room temp. – without losing adhesion 4 hours after taking out of the fuel
  • Heat resistance 121O C during 60 minutes – NO shade changes to Delta E = 1.
  • Adhesion to metal – 210kg/cm2
  • Humidity cabinet – 30  days in 100% humidity in 49 oC – no loss of adhesion  or damage to the film after 1 hr.  Out of cabinet.
  • Salt spray durability – 3000 hours with no corrosion occurs.
  • Thermal shock – without adhesion loses.
  • % Solids – 100%.
  • % pigment in paint – 2 kg. cooper powder for every liter epoxy mixture.
  • Flash point – non.
  • Drying time before departure – minimum 24 hours in shade with no exposure to sun.
  • Maximum dry time before departure – 5 days,
  • Final recommended thickness- 250-350 micron.
  • Average erosion per year – 5 micron.

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.

Contains:

  • Epoxy resins 100% solids self-polishing and hardeners.
  • Cooper oxide red-brown toxins.
  • Pure cooper powder 99% purity.
  • Special flexibility materials.
  • Additives

 Colors:

  • Red-brown cooper. Changes color to green in sea.

 Gloss:

  • Glossy-silky(Israel standard 935 chapter 309).

 Dry to the touch:

  • 30-60 minutes depends on environment temp. dry time in wheel- < 45 minutes (Israel standard 935 paragraph 304 amendment 2 ).

Drying between layers and final:

  • 1 hours, final: 24 hours,

 Putting the vessel back to water after painting:

  • Minimum 24 hours after painting last coat and drying in the shade.
  • Recommended waiting few days <5 before putting vessel in the water.
  • Before putting in the water sand lightly surface with scotch or gentle sand paper to discover the cooper before it touch the water.

 Application methods:

  • With roller mainly. Less suitable by brush and not comfortable by spray.
  • Can be spray with dilution of thinner 4/100 but while spraying no stops aloud. If spraying stops, clean the spray gun or airless immediately.

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.

Dilution:

  • With roller without dilution.
  • Airless -25% thinner 4/100 for spraying, out let pressure < 120 atm. spray distance < 25 cm. nozzle 0.018”

 Surface preparation:

  • Perfect cleaning from dust, dirt or grease or loose paint. Sand completely and wash with Degreezer Z for full oil and dirt removing. Wash with fresh water and wait for complete drying. If iron metal with rust – remove rust with metal brushes st-2level, if it is completely rusty – sand blast to level SA-2.5 and paint all paint layers as recommended.
  • Recommendations for paint systems for new painting (not renew):
  Steel ships with sand blasting Steel ships with no sand blast
First coat EPOXYDEN  HB19 Solcoat red –

50 mic. dry

EPOXYDEN Solcoat aluminum – 100 mic. dry
Second coat EPOXYDEN Solcoat aluminum – 100 mic. dry EPOXYDEN  HB19 Solcoat red –

100 mic. dry

Third coat EPOXYDEN  HB19 Solcoat red –

50 mic. dry

EPOXYDEN Solcoat aluminum – 100 mic. dry
Four coat EPOXYDEN  HB19 Solcoat grey –

50 mic. dry

EPOXYDEN  HB19 Solcoat grey –

50 mic. dry

5-6 coat EPOXYDEN COOPER antifouling 250-350 mic. dry EPOXYDEN COOPER antifouling 250-350 mic. dry

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.

  ALUMINUM VESSLES WITH SAND BLAST ALUMINUM VESSLES WITHOUT SAND BLAST
First coat EPOXYDEN WASH PRIMER clear yellow 50 MIC. dry EPOXYDEN WASH PRIMER clear yellow 50 MIC. dry
Second coat EPOXYDEN  HB19 Solcoat red –

100 mic. dry

EPOXYDEN  HB19 Solcoat red –

125 mic. dry

Third coat EPOXYDEN  HB19 Solcoat grey –

100 mic. dry

EPOXYDEN  HB19 Solcoat grey –

50 mic. dry

4-6 coat EPOXYDEN COOPER antifouling 250-350 mic. dry EPOXYDEN COOPER antifouling 250-350 mic. dry

 

FIBERGLASS BOATS, YACHTS, SHIPS WOODEN BOATS, YACHTS, SHIPS
First coat EPOXYDEN Solcoat aluminum – 50 mic. dry EPOXYDEN Solcoat aluminum –

50 mic. dry

Second coat EPOXYDEN  HB19 Solcoat grey –

100 mic. dry

EPOXYDEN  HB19 Solcoat grey –

75 mic. dry

Third coat EPOXYDEN  HB19 Solcoat red –

100 mic. dry

EPOXYDEN  HB19 Solcoat red –

75 mic. dry

4-6 coat EPOXYDEN COOPER  antifouling 250-350 mic. dry EPOXYDEN COOPER  antifouling

250-350 mic. dry

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.

Packaging:

  • 1 liter paint + 0.4 liter hardener + 0.7 liter cooper powder
  • 5 liter paint + 1 liter hardener + 1.8 liter copper powder.

Storage:

  • In a cool shaded place in room temp. with proper ventilation.
  • Keep lids tightly closed.

Shelf life:

  • 12 months in original package.

Tools cleaning:

  • Thinner 4/100-D at the end of painting.

Quality control:

  • In factory laboratories according to specifications.
  • COA and COC certificate.
  • ISO 9001-2015

EPOXYDEN SHIP COOPER ANTIFOULING

High build self-eroding 99% pure cooper and cooper oxide.