DENBERGLOSS FLOURESCENT LIGHT REFLECTING

A two-component elliptic polyurethane paint that is hard, luminous and reflective, for painting markings on floors, walls, plastics and metals. Reflects light in a glowing color.  For painting on a white epoxy primer. The color is sensitive to sunlight, it must be applied on a white epoxy or polyurethane base and it is recommended to cover it with a layer of varnish for  UV protection .

DENBERGLOSS FLOURESCENT   – POLYURETHANE  TWO COMPONENT LIGHT REFLECTING PAINT, GLOW AT LIGHT.

Characteristics:

• A strong and striking glow reflects light.
• Enables visible signage and guidance.
• Elliptical color with a smooth and hard finish.
• Very washable and repels dust and dirt.
• High hardness.
• Resistant to scratches and light mechanical damage, abrasion resistant.
• Resistant to various chemicals and solvents.
• The luminous pigment is sensitive to direct exposure to the sun and tends to fade, such areas must be repainted after the pigment has faded.
• Heat and cold resistance.
• Very high gloss.
• quick drying.
• Flexible for bending and hard for abrasion.
• Excellent adhesion to a white epoxy base.
• Easy to apply.
• Resistant to all external conditions, even freezing.
• Must be painted on a suitable white epoxy base.

Uses:

• As a color that stands out to the eye and shines for marking and orientation.
• As a color for direction and warning signs.
• And as a color to mark travel routes for forklifts in industrial plants.
• For painting floor areas in industry to mark areas and separate them for pedestrians and forklifts.

Two-component polyurethane fluorescent paint

Technical data:

• Theoretical coverage – 1 liter per 10 square meters.
• Practical coverage for required thickness – 1 liter per 5 square meters.
• Recommended wet layer thickness – 200 dry microns.
• Recommended dry layer thickness – 125 microns.
• Recommended number of layers – 2 minimum (for walls 2 layers of 60 microns)
• Flexibility – 100 micron film 1 mm (sheen)
• Density – 1.1-1.2 gm/cm ³
• Average viscosity A+B– 1-2 sec
• Stiffness – 10 Dg < (Ericsson)
• Abrasion – 120 microns – 3600 cycles (Gardner) ASTM
• Base to hard ratio – 2:1
• Pot life = working time from the moment of mixing B+A – 6> hours.
• Resistance to distilled water 24 hours – without loss of adhesion or corrosion one hour after removal from the liquid.
• Hydrocarbon resistance – no loss of adhesion one hour after removal from the liquid.
• and oil resistance 1250 24 hours at ^O ​​C 121- without loss of adhesion 4 hours after removal from the liquid.
• and hydraulic oil resistance 24 hours at 66 ^O C – no loss of adhesion 4 hours after removal from the liquid
• Resistance to jet fuel – 7 days at room temperature – no loss of adhesion 4 hours after removal from the liquid
• Heat resistance –  ^O  C121 for 60 minutes. No tone changes up to delta E =1.
• Humidity chamber – 30 days in 100% humidity at a temperature of  ^O C49 without loss of adhesion or damage to the film one hour after removal from the liquid
• Salt cell – 500 hours without the appearance of corrosion.
• Thermal market – no loss of adhesion.
• % solids by volume – 66.6%

Color:

• Yellow, red, blue, green, silver white.
• Intermediate shades: pink, orange, turquoise, purple

Gloss:

• brilliant.

Packing:

• 3.35+1.65 = 5 liters. 5+2.5 = 7.5 liters, 10+5 = 15 liters.

This technical specification is for  non-binding general information only. 

Produced by  Denber Paints and Coatings Israel Ltd. , and